Reaction mechanisms of wood ash for use as a partial cement replacement
Peer reviewed, Journal article
Accepted version
Åpne
Permanent lenke
https://hdl.handle.net/11250/2736044Utgivelsesdato
2021Metadata
Vis full innførselSamlinger
Originalversjon
10.1016/j.conbuildmat.2021.122889Sammendrag
An increase in the produced amounts of wood ashes (WAs) is seen worldwide. In this study, the potential use of two representative WAs as a partial cement replacement is investigated. The WAs originate from combustion of wood chips by grate combustion (WA1) and circulating fluidised bed combustion (WA2). Both WAs were found to possess hydraulic properties, no pozzolanic properties were detected. A substantial difference in strength development was observed between WA1 and WA2 attributed to the phases formed; WA2 contributing the most, ettringite in addition to other phases were formed, while gypsum formed in WA1 pastes.