Loading rate effects on the fracture of Ni/Au nano-coated acrylic particles
Journal article, Peer reviewed
Published version
Åpne
Permanent lenke
http://hdl.handle.net/11250/2468542Utgivelsesdato
2012Metadata
Vis full innførselSamlinger
Sammendrag
Mechanical failure of monodisperse Ni/Au coated acrylic particles has been investigated by individual compression tests using nanoindentation-based technique equipped with a flat diamond punch. We have found that both fracture property and morphology of particles depend on the compression loading rate. The breaking strain of the metal coating decreases with increasing loading rate, while the breaking stress increases. Two obvious fracture patterns with cracking in meridian or latitude direction are identified according to the loading rate, and attributed respectively to tension- or bending dominated deformation of the coating. The findings reported here give a significant guiding to the manufacture design of metal coated polymer particles for Anisotropic Conductive Adhesive (ACA) packaging.