CS-AFM study on Pb-induced degradation of passive film on nickel-based alloy in high temperature and high pressure water
(Journal article, 2018)The degradation mechanism of trace Pb on nickel-based alloy passive film in pure water at 270 is researched by surface analysis techniques and calculations. Experimental results show that Pb reduces the oxygen content and ... -
Environmentally assisted degradation of spinodal copper alloy C72900
(Journal article; Peer reviewed, 2018)In this work, a spinodal Copper alloy – C72900, was tested to investigate the resistance against environmentally assisted degradation. The material was tested according to ISO 15156-3 Level V in sour H2S solution and to ... -
Stress corrosion cracking of Ni2MnGa magnetic shape memory alloy in water and moist atmosphere
(Journal article; Peer reviewed, 2009)We prepared two kinds of cracks (surface cracks and transfixion cracks) to in situ study stress corrosion cracking of seven-layered (which is denoted as 7 M or 14 M) off-stoichiometric Ni2MnGa magnetic shape memory alloy ...