Effect of Zr and Er on the microstructure, mechanical and electrical properties of Al-0.4Fe alloy
Peer reviewed, Journal article
Accepted version
![Thumbnail](/ntnu-xmlui/bitstream/handle/11250/2983680/Plain%2btext%2bEffect%2bof%2bZr%2band%2bEr%2bon%2bthe%2bmicrostructure%252C%2bmechanical%2band%2belectrical%2bproperties%2bof%2bAl-0%252C4%2bFe%2balloy_2021.pdf.jpg?sequence=6&isAllowed=y)
Åpne
Permanent lenke
https://hdl.handle.net/11250/2983680Utgivelsesdato
2021Metadata
Vis full innførselSamlinger
- Institutt for materialteknologi [2549]
- Publikasjoner fra CRIStin - NTNU [38127]
Sammendrag
The effect of Zr and Er on the microstructure, electrical conductivity and mechanical properties of Al-0.4Fe alloy was investigated using optical microscope (OM), scanning electron microscope (SEM), electron back-scattered diffraction (EBSD), transmission electron microscope (TEM) and energy dispersive x-ray spectroscopy (EDS). It is revealed that both of the Zr and Er could inhibit the recrystallization process of Al-0.4 wt %Fe alloy due to the formation of Al3Zr or Al3Er particles. Zr is more recrystallization-resistant than Er due to the preferential precipitation of Al3Zr. Both of the Zr and Er could modify the morphology of Al3Fe particle from needle-like to sphere-like or rod-like, which reduce the negative effect of Al3Fe phase. Zr could significantly refine dendrites of the Al-0.4Fe alloy, while Er shows a negligible effect on dendrite refining due to the delayed formation of Al3Er during solidification. However, the low solubility of Er is beneficial for strength and electrical properties of Al-0.4Fe alloy. In consideration of strength and electrical conductivity, the Al-0.4Fe-0.2Er is selected as the best alloy among the four alloys, which shows a yield strength of 145 MPa, elongation at fracture of 8% and electrical conductivity of 61.2 %IACS after cold-rolling. The results provide an insight in design high strength, high conductive aluminum conductor material.