Hydrogen susceptibility of an interstitial equimolar high-entropy alloy revealed by in-situ electrochemical microcantilever bending test
Peer reviewed, Journal article
Accepted version
Åpne
Permanent lenke
https://hdl.handle.net/11250/2650544Utgivelsesdato
2019Metadata
Vis full innførselSamlinger
Sammendrag
Hydrogen effect on an interstitial CoCrFeMnNi high-entropy alloy was investigated by micro-cantilever bending tests with pre-notched plane as a case study. Results showed sharp mode I cracks on plane bisecting two planes in hydrogen-charged cantilevers, which was explained by hydrogen-assisted defects formation and hydrogen pins dislocation motion.