In situ small-scale hydrogen embrittlement testing made easy: An electrolyte for preserving surface integrity at nano-scale during hydrogen charging
Hajilou, Tarlan; Hope, Malin S.B.; Hossein Zavieh, Amin; Kheradmand, Nousha; Johnsen, Roy; Barnoush, Afrooz
Journal article, Peer reviewed
Accepted version
![Thumbnail](/ntnu-xmlui/bitstream/handle/11250/2600943/Tarlan_Hajilou_Electrolyte_revision.pdf.jpg?sequence=7&isAllowed=y)
View/ Open
Date
2018Metadata
Show full item recordCollections
Original version
International journal of hydrogen energy. 2018, 43 (27), 12516-12529. 10.1016/j.ijhydene.2018.04.168Abstract
An electrolyte for electrochemical hydrogen charging of corrosion-susceptible alloys is developed, which preserves the surface integrity at nano-scale by minimizing the surface roughness alternation. To assure the formation and adsorption of the hydrogen from the electrolyte, permeation tests were performed on Fe 3 wt%Si ferritic steel. X-ray photoelectron spectroscopy method was used to check the effect of the glycerol-based solution on the chemical composition of the sample surface. The surface analysis revealed minimal chemical and topography alteration on the surface after different electrochemical treatments. Various types of in situ small-scale mechanical tests such as nano-indentation, micro-pillar compression, and micro-cantilever bending tests were performed inside this electrolyte while the samples being charged with hydrogen under cathodic potential. These small-scale mechanical tests showed that the solution facilitates studying hydrogen embrittlement in nano- or micro-scale.