Impact of Accelerated Carbonation on Microstructure and Phase Assemblage
Journal article, Peer reviewed
Accepted version
Permanent lenke
http://hdl.handle.net/11250/2594341Utgivelsesdato
2018Metadata
Vis full innførselSamlinger
Sammendrag
The paper summarizes preliminary results on characterization of the microstructure and phase
assemblage of mortar and concrete samples containing Portland and Portland -fly ash cement
carbonated at either natural conditions, 60% RH and 1% CO2, 90% RH and 5% CO2 or 60% RH
and 100% CO2. Different characterization techniques were used: thermogravimetric
analysis to study the solid phases, SEM-EDS point analysis to investigate the chemical composition of the solid phases, optical microscopy to investigate the microstructure, and cold water extraction to characterize the chemical composition of the pore solution. The combined results on microstructure and phase assemblage indicate that carbonation up to 5% CO2 appears representative for natural carbonation. Pore solution analysis revealed similar trends for the three accelerated carbonation conditions.