Effect of low Cu addition and thermo-mechanical history on precipitation in Al-Mg-Si alloys
Journal article
Submitted version
Permanent lenke
http://hdl.handle.net/11250/2474434Utgivelsesdato
2014Metadata
Vis full innførselSamlinger
- Institutt for fysikk [2701]
- Publikasjoner fra CRIStin - NTNU [38525]
Originalversjon
Materials Science Forum. 2014, 794-796 1014-1019. 10.4028/www.scientific.net/MSF.794-796.1014Sammendrag
The effect of cooling rate after solution heat treatment and its combination with 1% pre-deformation on precipitation hardening in two Al-Mg-Si alloys is investigated by transmission electron microscopy (TEM), and related to material hardness. Two alloys have been used, one Cu-free and the other with low Cu additions (~0.1 wt%), both having the same amounts of other solutes. A double peak hardness evolution during an isothermal heat treatment was observed with slow cooling after solution heat treatment. This effect was less pronounced in the Cu-added alloy. The 1% pre-deformation also made this effect less pronounced, but it led to faster initial hardness evolution and delayed over-aging. Maximum hardness was not influenced by cooling rate and the pre-deformation. Hardness was directly related to precipitate number densities.