Comparison of cathodic delamination of poly(n-alkyl methacrylates) on iron
Journal article, Peer reviewed
Accepted version
Date
2017Metadata
Show full item recordCollections
- Institutt for materialteknologi [2553]
- Publikasjoner fra CRIStin - NTNU [38525]
Original version
Materials and corrosion - Werkstoffe und Korrosion. 2017, 68 1326-1332. 10.1002/maco.201609289Abstract
Cathodic delamination is measured on iron surfaces covered with different poly(n-alky methacrylates), where the alkyl is an n-CnH2n + 1 (n = 1, 4, 18) group. The polymers are prepared by free radical polymerization in solution and spin coated individually on iron. The materials were characterized by infrared (IR) spectroscopy, ellipsometry, and contact angle measurements. Barrier properties in potassium chloride were obtained by electrochemical impedance spectroscopy (EIS). Artificial defects in the polymer model coatings were exposed to 1 M potassium chloride as corrosive medium, and cathodic delamination was measured by a scanning Kelvin probe. The surface wettability decreases as the size of the pending alkyl group in the backbone increases. The same chemical feature shows also an effect on the cathodic delamination and on the electrochemical impedance results. Delamination is roughly twice as fast when n = 1, compared to n = 4 and n = 18. The difference in delamination rate between the latter two polymers is small.