Permanent effect of a cryogenic spill on fracture properties of structural steels
Journal article, Peer reviewed
Published version
Permanent lenke
http://hdl.handle.net/11250/2457756Utgivelsesdato
2015Metadata
Vis full innførselSamlinger
- Institutt for materialteknologi [2549]
- Publikasjoner fra CRIStin - NTNU [38294]
Originalversjon
IOP Conference Series: Materials Science and Engineering. 2015, 102 . 10.1088/1757-899X/102/1/012004Sammendrag
Fracture analysis of a standard construction steel platform deck, which had been exposed to a liquid nitrogen spill, showed that the brittle fracture started at a flaw in the weld as a consequence of low-temperature embrittlement and thermal stresses experienced by the material. In the present study, the permanent effect of a cryogenic spill on the fracture properties of carbon steels has been investigated. Charpy V-notch impact testing was carried out at 0 °C using specimens, from the platform deck material. The average impact energy appeared to be below requirements only for transverse specimens. No pre-existing damage was found when examining the fracture surfaces and cross sections in the scanning electron microscope. Specimens of the platform deck material and a DOMEX S355 MCD carbon steel were tensile tested immersed in liquid nitrogen. Both steels showed a considerable increase in yield- and fracture strength and a large increase in the Lüders strain compared to the room temperature behavior. A cryogenic spill was simulated by applying a constant tensile force to the specimens for 10 min, at -196 C. Subsequent tensile tests at room temperature showed no significant influence on the stress-strain curve of the specimens. A small amount of microcracks were found after holding a DOMEX S355 MCD specimen at a constant force below the yield point. In a platform deck material tensile tested to fracture in liquid nitrogen, cracks associated with elongated MnS inclusions were found through the whole test region. These cracks probably formed as a result of the inclusions having a higher thermal contraction rate than the steel, causing decohesion at the inclusion-matrix interface on cooling. Simultaneous deformation may have caused formation of cracks. Both the microcracks and sulphide related damage may give permanently reduced impact energy after a cryogenic exposure.