Regenerated cellulose based carbon membranes for CO2 separation; Durability and aging under miscellaneous environments
Journal article, Peer reviewed
Accepted version
Permanent lenke
http://hdl.handle.net/11250/2584714Utgivelsesdato
2018Metadata
Vis full innførselSamlinger
Originalversjon
https://doi.org/10.1016/j.jiec.2018.10.037Sammendrag
Predictive models regarding the aging effect on membrane separation properties are required to estimate the membrane life time with acceptable permeability and selectivity for the respective application. The current article is reporting an insight into this topic regarding the aging of regenerated cellulose-based carbon hollow fibres (CHF) mounted in a membrane module when they were exposed to real biogas in three different fields. CHF were exposed to biogas for almost one year with H2S content extending from 0 to 2400 ppm, and gas permeation tests for single gases, N2, CO2, CH4, and O2 were analysed periodically at the membrane production facility. CHF storage methods under miscellaneous dry environments like air, vacuum, CO2, etc. were studied. The air flow through bore side of the CHF under controlled conditions had a regenerative effect on the membrane permeability, and the membrane performance was quite steady until after 150 days under laboratory environment.