Cathodic delamination kinetics of thin polystyrene model coatings bound to zinc via organosilanes

Iqbal, Danish; Rechmann, Julian; Bashir, Ali; Sarfraz, Adnan; Altin, Abdulrahman; Erbe, Andreas
Journal article, Peer reviewed
Accepted version
Thumbnail
Åpne
Iqbal (648.8Kb)
Permanent lenke
http://hdl.handle.net/11250/2588805
Utgivelsesdato
2018
Metadata
Vis full innførsel
Samlinger
  • Institutt for materialteknologi [1986]
  • Publikasjoner fra CRIStin - NTNU [26648]
Originalversjon
Materials and corrosion - Werkstoffe und Korrosion. 2018, 70 481-491.   10.1002/maco.201810395
Sammendrag
The cathodic delamination of poly(styrene) [PS] model coatings from oxidecovered

zinc has been evaluated by scanning Kelvin probe (SKP). Linear and

acrylate cross-linked PS model coatings covalently bound to zinc oxide via

Zn─O─Si bonds have been prepared. PS was prepared by thermally initiated free

radical polymerization in the presence of vinyltrimethoxy silane modified zinc.

Cross-linkers ethylene glycol diacrylate (EDA) and hexanediol diacrylate (HDA)

were used in some preparations. Resulting polymers are 8–15 nm thick. PS model

coatings show a delamination rate of only ≈20% of that of comparable

poly(methyl methacrylate) [PMMA] samples. The slower cathodic delamination

of PS is attributed to denser chain packing and higher amounts of hydrophobic

moieties, leading to a reduction in penetration of corrosive species. As opposed to

the situation in PMMA, the addition of HDA increases the delamination rate, due

to its flexible chains and hydrophilic groups. The lowest delamination rate is

observed in the presence of 25% EDA. Consequently, ester hydrolysis of acrylates

accelerates delamination, it is however not the main factor in cathodic

delamination of such thin model system.
Utgiver
Wiley
Tidsskrift
Materials and corrosion - Werkstoffe und Korrosion

Kontakt oss | Gi tilbakemelding

Personvernerklæring
DSpace software copyright © 2002-2019  DuraSpace

Levert av  Unit
 

 

Bla i

Hele arkivetDelarkiv og samlingerUtgivelsesdatoForfattereTitlerEmneordDokumenttyperTidsskrifterDenne samlingenUtgivelsesdatoForfattereTitlerEmneordDokumenttyperTidsskrifter

Min side

Logg inn

Statistikk

Besøksstatistikk

Kontakt oss | Gi tilbakemelding

Personvernerklæring
DSpace software copyright © 2002-2019  DuraSpace

Levert av  Unit