dc.description.abstractIn the search to understand the functional capabilities and limitations of fused deposition modelling (FDM) manufactured components, control over their structural behaviour is crucial. For example, voids introduced during the production phase are a large contributor to anisotropy, yet the magnitude of this contribution remains unquantified. As a baseline model for quantifying strength reduction due to process-induced voids, a statistical method for evaluation of the minimum residual (net) cross section is proposed and tested. Our new method serves to predict the reduction in ultimate tensile strength of transversely printed specimens relative to solid or longitudinally printed specimens, based on void sizes identified from microscopy images of the centre plane of a tensile specimen. ImageJ is used to identify void sizes from the microscopy images, and residual cross sections are determined using a bit counting MATLAB script. From the distribution of residual cross sections, the weakest link for a given sample size is estimated. The accuracy of the proposed method is determined through comparison with experimental test data for samples of polylactic acid (PLA). The results reveal a close yet slightly under-predicted strength estimate, which for the case considered predicted approximately 5 MPa (12%) lower strength than observed in the experiments. Based on our findings, we have established evidence that the anisotropic behaviour of FDM specimens in PLA can to a large extent be explained by the reduction in residual cross section. This implies that other effects such as fracture mechanics and atomic diffusion of polymer chains play a secondary role for the phenomena observed.nb_NO
dc.language.isoengnb_NO
dc.publisherSpringer Verlagnb_NO
dc.rightsNavngivelse 4.0 Internasjonal*
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/deed.no*
dc.titleThe effects of voids on structural properties of fused deposition modelled parts: a probabilistic approachnb_NO
dc.title.alternativeThe effects of voids on structural properties of fused deposition modelled parts: a probabilistic approachnb_NO
dc.typeJournal articlenb_NO
dc.typePeer reviewednb_NO
dc.description.versionpublishedVersionnb_NO
dc.source.pagenumber3607-3618nb_NO
dc.source.volume97nb_NO
dc.source.journalThe International Journal of Advanced Manufacturing Technologynb_NO
dc.source.issue9-12nb_NO
dc.identifier.doi10.1007/s00170-018-2148-x
dc.identifier.cristin1614525
dc.description.localcode© The Author(s) 2018 Open Access. This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/)nb_NO
cristin.unitcode194,64,92,0
cristin.unitnameInstitutt for maskinteknikk og produksjon
cristin.ispublishedtrue
cristin.fulltextoriginal
cristin.qualitycode2


Tilhørende fil(er)

Thumbnail

Denne innførselen finnes i følgende samling(er)

Vis enkel innførsel

Navngivelse 4.0 Internasjonal
Med mindre annet er angitt, så er denne innførselen lisensiert som Navngivelse 4.0 Internasjonal