Formation of aluminium carbide in Hall-Héroult electrolysis cell environments

Novák, Bronislav; Ratvik, Arne Petter; Wang, Zhaohui; Grande, Tor
Journal article, Peer reviewed
Accepted version
Thumbnail
Åpne
Novak-Formation+of+aluminium+carbide+in+hall+heroult+electrolysis+cell+environments-TMS2018-final.pdf (487.5Kb)
Permanent lenke
http://hdl.handle.net/11250/2581740
Utgivelsesdato
2018
Metadata
Vis full innførsel
Samlinger
  • Institutt for materialteknologi [1571]
  • Publikasjoner fra CRIStin - NTNU [19877]
Originalversjon
Light Metals. 2018, 2018 1215-1222.   10.1007/978-3-319-72284-9_159
10.1007/978-3-319-72284-9_159
Sammendrag
The formation and dissolution of aluminium carbide under conditions similar to the chemical and electrochemical environments in the Hall-Héroult process were studied in laboratory cells, including cells with reversed polarization. The cross sections of the various electrochemical cells after the electrolysis experiments were characterized by optical and electron microscopy. A relatively dense layer of aluminium carbide was observed on the carbon cathode surface under conventional electrolysis conditions. Aluminium carbide was also found in the pores of the cathode together with bath, while only bath was found in the anode. While the direct chemical reaction between carbon and aluminium to form Al4C3 is slow, the polarisation of the cathode and electrolysis were demonstrated to have a pronounced effect on the formation of Al4C3. The present finding is discussed with emphasis of the difference between chemical and electrochemical formation of Al4C3 and the importance of the initial presence of aluminium at the cathode.
Utgiver
Springer Verlag
Tidsskrift
Light Metals

Kontakt oss | Gi tilbakemelding

Personvernerklæring
DSpace software copyright © 2002-2019  DuraSpace

Levert av  Unit
 

 

Bla i

Hele arkivetDelarkiv og samlingerUtgivelsesdatoForfattereTitlerEmneordDokumenttyperTidsskrifterDenne samlingenUtgivelsesdatoForfattereTitlerEmneordDokumenttyperTidsskrifter

Min side

Logg inn

Statistikk

Besøksstatistikk

Kontakt oss | Gi tilbakemelding

Personvernerklæring
DSpace software copyright © 2002-2019  DuraSpace

Levert av  Unit