dc.date.issued2015
dc.identifier.isbn978-82-326-1193-5
dc.identifier.issn1503-8181
dc.identifier.urihttp://hdl.handle.net/11250/2364812
dc.description.abstractSolar cells are among the most promising technologies for development of sustainable power generation in terms of environmental impact and resource availability, and crystalline silicon cells dominate the present market expansion. Cost reductions are still necessary for this technology to become a major global energy producer. Development of metallurgical refining processes for solar grade silicon has potential to drastically decrease energy consumption, but face challenges to effectively remove the important impurities boron and phosphorus. For boron removal, refining by an oxidizing reactive gas show potential for low energy consumption and promising refining rates. Previous investigation of reactive gas boron removal is limited, while related plasma refining has been developed to pilot scale. This experimental study seeks to reveal the potential and limits of reactive gas refining for boron removal. First and foremost at a fundamental level to understand the removal process and what determines the rate of removal. Boron was removed from high-purity silicon and metallurgical grade silicon at 1500-1800 ◦C by blowing steam in hydrogen and/or argon onto the melt surface. The rate of boron removal was calculated from inductively coupled plasma mass spectrometry analyzes of the boron content in samples periodically extracted from the melt. The fastest rate of boron removal was achieved at the highest gas flow rate. Increasing the partial pressure of steam was also found important to increase the removal rate and simultaneously reduce gas consumption. Supply of steam as the oxidizing agent to the interface is the only identified rate determining step for boron removal, like for active oxidation of silicon to SiO gas at the interface. At least 50% of the steam in the feed did not reach the surface in representative experiments and this is attributed to essentially stoichiometric Reactions (0.1) in the gas and (0.2) for active oxidation of silicon at the interface. Diffusion of steam accounts for increasing losses with increasing gas flow rate. The fraction of steam in the feed gas that was supplied to the melt surface was estimated by comparing weightloss by active silicon oxidation in experiments to equilibrium in Reaction (0.2) if all of the feed gas had reacted. H2O + SiO = SiO2 (s) + H2 (0.1) Boron removal in experiments was found to proceed at equilibrium between HBO in the gas flow and boron in the melt, which was determined from the estimated supply of steam to the interface Reactions (0.2) and (0.3). No resistance was identified for the mass transfer of boron as such. H2O + [Si] −−→ ←− SiO + H2 (0.2) [B] + SiO + 1 2 H2 ¬ HBO + [Si] (0.3) Equilibrium at the interface also agreed with observations that silica passivation forms if the steam supply is above the saturation pressure of SiO in Reaction (0.4). Silica formed continuous layers and stopped boron removal if formed on the entire surface. A clean melt surface could be maintained with steam partial pressures less than twice the saturation pressure of SiO at the temperature of the melt. Additionally, CO reacted to SiC particles on the surface and was found less effective for boron removal than steam. Atmospheric partial pressure of steam was tested at 1800 ◦C, and exploration of such conditions is suggested for further developments. 2 SiO ¬ [Si] + SiO2 (s/l) (0.4)nb_NO
dc.language.isoengnb_NO
dc.publisherNTNUnb_NO
dc.relation.ispartofseriesDoctoral thesis at NTNU;2015:268
dc.titleBoron removal from silicon by steam and hydrogennb_NO
dc.typeDoctoral thesisnb_NO
dc.subject.nsiVDP::Technology: 500::Materials science and engineering: 520nb_NO