Nanostructural Analysis of Co-Re/γ-Al2O3 Fischer-Tropsch Catalyst by TEM and XRD
Dehghan-Niri, Roya; Tsakoumis, Nikolaos E.; Voronov, Alexey; Holmen, Anders; Holmestad, Randi; Vullum, Per Erik; Borg, Øyvind; Rytter, Erling; Rønning, Magnus; Walmsley, John (Journal article; Peer reviewed, 2022)A rhenium promoted Fischer-Tropsch (FT) cobalt catalyst supported on γ-Al2O3 has been investigated by Transmission Electron Microscopy (TEM) and X-ray Diffraction (XRD), before and after reduction. Electron diffraction, ... -
Nickel and Iron Poisoning of Copper Based Methanol Synthesis Catalysts
Wigum, Stine Hagen (Master thesis, 2015)Discharged methanol synthesis catalysts are known to contain various amounts of nickel and iron. The purpose of this master thesis was to study nickel and iron poisoning of commercial copper based methanol synthesis catalysts ... -
Role of Alumina Support in Cobalt Fischer-Tropsch Synthesis
Borg, Øyvind (Doktoravhandlinger ved NTNU, 1503-8181; 2007:56, Doctoral thesis, 2007) -
Significance of C3 Olefin to Paraffin Ratio in Cobalt Fischer–Tropsch Synthesis
Rytter, Erling; Yang, Jia; Borg, Øyvind; Holmen, Anders (Peer reviewed; Journal article, 2020)The ratio between propene and propane (C3 o/p) during Fischer–Tropsch synthesis (FTS) has been analyzed based on both literature reports and experiments for five catalysts. The latter comprise four cobalt catalysts on ... -
Water as key to activity and selectivity in Co Fischer-Tropsch synthesis: γ-alumina based structure-performance relationships
Rytter, Erling; Borg, Øyvind; Tsakoumis, Nikolaos; Holmen, Anders (Journal article; Peer reviewed, 2018)Thirteen γ-alumina supports with different pore sizes and pore size distributions have been impregnated with cobalt and rhenium. The catalysts were tested for Fischer-Tropsch synthesis (FTS) under dry and enhanced water ... -
X-ray absorption, X-ray diffraction and electron microscopy study of spent cobalt based catalyst in semi-commercial scale Fischer-Tropsch synthesis
Tsakoumis, Nikolaos; Dehghan-Niri, Roya; Rønning, Magnus; Walmsley, John; Borg, Øyvind; Rytter, Erling; Holmen, Anders (Peer reviewed; Journal article, 2014)Calcined, reduced and spent Co-Re/γ-Al2O3 catalysts for Fischer–Tropsch synthesis (FTS) were characterized and compared. Co-K-edge and Re-LIII-edge X-ray absorption near edge structure (XANES), X-ray powder diffraction ... -
α-alumina as catalyst support in Co Fischer-Tropsch synthesis and the effect of added water; encompassing transient effects
Rytter, Erling; Borg, Øyvind; Enger, Bjørn Christian; Holmen, Anders (Peer reviewed; Journal article, 2019)Three catalyst supports containing from 84 to 100% α-alumina prepared by heat treatment of γ-alumina have been impregnated with cobalt and rhenium. The catalysts were tested for Fischer-Tropsch synthesis (FTS) under dry ...