(Scanning) Transmission Electron Microscopy Studies of Grain Boundary Segregation relevant to Intergranular Corrosion in Al-Mg-Si-Cu Alloys
Doctoral thesis
View/ Open
Date
2015Metadata
Show full item recordCollections
- Institutt for fysikk [2703]
Abstract
The effect of the alloy composition on the susceptibility to intergranular corrosion
in Al-Mg-Si-Cu alloys has been investigated by Transmission Electron
Microscopy. The main focus of this thesis has been the effect of Mg:Si-ratio
and the effect of Mn-content on the intergranular corrosion, since Mg and
Si are the main alloying elements of the 6xxx alloys and Mn is a common
alloying element.
The addition of 0.40 wt% Cu to a 6082 alloy increases the hardness of the
alloy by approximately 10 HV in all ageing conditions. The susceptibility
to intergranular corrosion is also increased in a slightly underaged condition
due to the formation of an enriched layer of Cu at the grain boundary.
By adjusting the Mg:Si-ratio from 0.87 in the 6082 alloy to 2.00, the susceptibility
to intergranular corrosion is reduced. In this Mg-rich alloy, an
enriched layer of both Mg and Cu was observed at the grain boundary.
The presence of Mg reduces the cathodic potential created by the Cu and
reduces the potential difference between the grain boundary layer and the
adjacent depleted zone.
In leaner alloys, a reduced susceptibility to intergranular corrosion is observed
when the Mg:Si-ratio is increased from 0.80 to 2.90. The alloy with
a high Mg:Si-ratio has the same amount of excess Mg as the 6082-type alloy
with a ratio of 2.00. The Mg-rich lean alloy shows an enriched layer of both
Mg and Cu at the grain boundary, while the Si-rich only shows an enriched
layer of Cu. Once again, the Mg+Cu has a reduced electrochemical potential
compared to the pure Cu layer in the Si-rich alloy and the resistance to
intergranular corrosion is increased.
By removing the Mn from the 6082-type alloy with excess Mg, a fully recrystallized
structure with small grains and an aspect ratio close to 1 is
achieved. This alloy show significant susceptibility to intergranular corrosion, even though the enriched grain boundary layer contain both Mg
and Cu. It is likely that the grain structure makes it easier for the corrosion
attack to penetrate more deeply into the sample since most of the
grain boundaries are approximately perpendicular to the surface. In the
Mn-containing alloy, most of the interior grains are very large and have an
aspect ratio >> 1. The intergranular corrosion attacks can only propagate
parallel to the surface and the penetration depth is low. This underlines
the geometrical aspects of intergranular corrosion in alloys where the grain
boundary chemistry is otherwise similar.
In a very Si-rich version of the 6082-type alloy, there is still only observed
an enriched layer of Cu. The absence of an enriched layer of Si is not yet
understood, but more quantitative work needs to be done. The Si might
all disappear to the grain boundary precipitates and dispersoids, but that
investigation has been beyond the scope of this work.
It has not been found any periodicity or structure to the enriched layer at the
grain boundary, so the main theory at the moment is that it is not periodic.
The equipment needed to investigate this have only recently become available
and there are some issues with orienting the sample perfectly, meaning
that so far it is too early to conclude whether there is any periodicity in the
enriched boundary layer or not.