How calcium prevents precipitation hardening in Al–Mg–Si alloys
Journal article
Submitted version
Permanent lenke
http://hdl.handle.net/11250/2492468Utgivelsesdato
2013Metadata
Vis full innførselSamlinger
- Institutt for fysikk [2650]
- Publikasjoner fra CRIStin - NTNU [37175]
Sammendrag
We have investigated the effect on precipitate microstructure and hardness upon adding small amounts of Ca to a base Al–Mg–Si alloy. The main investigative techniques were transmission and scanning electron microscopy. We found that large Ca-containing particles with composition CaAl2Si2 form during the production stages of the alloy. The particles leave less Si available in solid solution for the nucleation of hardening precipitates, leading to a coarser microstructure consisting of less coherent precipitates. The resulting hardness decrease is measurable for alloys containing more than 60 at ppm of Ca.