Effect of room temperature storage time on precipitation in Al-Mg-Si(-Cu) alloys with different Mg/Si ratios
Journal article, Peer reviewed
Accepted version
Åpne
Permanent lenke
http://hdl.handle.net/11250/2482880Utgivelsesdato
2012Metadata
Vis full innførselSamlinger
- Institutt for fysikk [2698]
- Publikasjoner fra CRIStin - NTNU [38278]
Originalversjon
International Journal of Materials Research - Zeitschrift für Metallkunde. 2012, 103 (8), 948-954. 10.3139/146.110795Sammendrag
The effect of natural ageing time before artificial ageing has been investigated in four Al – Mg – Si(– Cu) alloys, with 0.4 % Mg + 0.8 % Si and 0.8 % Mg + 0.4 % Si, both with and without 0.14 at.% Cu. The precipitate microstructure was quantified by means of transmission electron microscopy. Varying the storage time before ageing for 170 min at 200 °C, we observe an initial hardness increase after minutes, a decrease after several hours and another increase after weeks. The hardness decrease was most pronounced in the Mg-rich Cu-free alloy, caused by a reduced precipitate volume fraction. Adding Cu produces finer „microstructures, higher hardness and reduces the negative effect of natural ageing regardless of the Mg/Si ratio of the alloy. With 1 week storage, an increase in the fraction of the Cu-containing precipitates L and Q was observed in the Cu-containing Si-rich and Mg-rich alloys respectively.